1. The temperature of zinc liquid is generally controlled at around 440-460℃. If the heating equipment has poor performance, the temperature distribution of zinc liquid will be uneven, which will affect the thickness of the zinc layer.
2. When the new steel grating is placed in the zinc liquid, the temperature of the zinc liquid will drop locally. If the heating power is not adjusted in time, the thickness of the zinc layer will also be uneven.
3. The immersion time is an important factor affecting the thickness of the zinc layer.
4. The complexity of the shape of the steel grating will affect the thickness of the zinc layer.
5. The purity of the zinc liquid will affect the quality and thickness of the zinc layer. If the zinc liquid contains more impurities, such as iron, lead, etc., it will change the properties of the zinc liquid.

1. The influence of the zinc liquid temperature. When the temperature of the zinc liquid is lower than 430℃, the diffusion rate of zinc and iron is low, and it is not easy to generate a sufficient iron-zinc alloy layer, so the entire coating is thin; when the temperature is 460℃, the zinc layer thickens, and when the temperature continues to rise, the zinc liquid becomes thinner and the zinc layer becomes thinner. Therefore, the temperature of the zinc liquid must be strictly controlled to ensure the stability of the quality of the steel grating.
2. The influence of the residence time of the steel grating in the zinc liquid. The residence time of the steel grating in the zinc liquid has a certain time range, which is determined according to the thickness of the steel grating. As the galvanizing time increases, the coating thickness will increase, but excessive extension of the galvanizing time will make the zinc layer brittle, which will affect the quality.
3. Influence of the extraction method of steel grating from zinc liquid. When the galvanized parts are drawn out of the zinc liquid, they should be drawn out vertically, and when the steel grating is drawn out at an angle, the zinc layer is thin. Therefore, the steel grating should be drawn out vertically when it is drawn out of the zinc pot.

Answers

• 
  What material is A36? 13/01/2025 15:48:34
• 
  How to deal with the excessive bending of steel bars? 13/01/2025 11:46:57
• 
  310S stainless steel plate density, main components, and properties? 10/01/2025 16:00:13
• 
  What is the material of carbon seamless steel pipe? 10/01/2025 04:34:56
• 
  Why is the thickness of the galvanized layer of the steel grating insufficient? 08/01/2025 15:51:12